T-S is a hard plate with a front layer made of a finely dispersed wood pulp .
DVPO-B is a hard fiberboard with paint coating; colors: white, black, beige.
Plate format, mm: 2745x1700x3. 2 ; 2745x1700x2. 5.
Physical and mechanical characteristics of A Group plates:
Density: 850-1100 kg/m3,
Bending strength: not less than 38 MPa,
Swelling thickness in 24 hours: not higher than 20%,
Humidity: 4-10%,
Water absorption by the front surface in 24 hours — no more than 11%..
Fiberboard is shipped in unpackaged and packaged form. The package of fiberboard consisting of 100 plates is installed on a wooden pallet, lined around the perimeter with billets of B group fiberboard and tied with steel or polyethylene packaging string, using plastic corners to protect the upper plates from crushing with the tape.
Precise slicing is possible according to customer’s specification.
There are certificates of the Republic of Belarus and the Russian Federation.
Fiberboard plates have good operational characteristics, thanks to which they have become a universal material for various types of work: from the containers manufacture to the furniture production. Fiberboard is made of finely dispersed wood pulp, compressed under high temperature. The advantages of fiberboard are high strength, durability, resistance to mechanical impact, low weight, ease of processing and low price. It is also possible to apply a white or beige paint covering on the front surface.
Fiberboard is universal material for any of your needs!
|
Parameter name |
Nominal value |
| length, mm |
|
| width, mm |
|
| thickness, mm PA mark plate PS-A mark plate |
|
| straightness of edges |
|
| squareness of edges |
|
| density, kg/m3 |
|
| Bending strength, MPa for P-A plates with a thickness of 10 mm, 12 mm |
|
| Bending strength, MPa for P-A plates with a thickness of 16 mm, 18 mm |
|
| Bending strength, MPa for P-A plates with a thickness of 22 mm, 24 mm |
|
| Bending strength, MPa for P-A plates with a thickness 26 mm |
|
| Bending strength, MPa for PS-A plates with a thickness 18 mm |
|
| Swelling, % for P-A plates(all thicknesses) for P-A, B plates(all thicknesses, increased water resistance) for PS-A plates(18 mm thick) |
|
| Density, kg/m3 for P-A plates for PS-A plates |
|
| Formaldehyde emission class |
|
According to GOST 10632-2007, the first-class plates should not have recesses (projections) or scratches, paraffin, tar spots, chipping edges, grinding defects. All of the above defects, in turn, are limited for the second-class plates.
For avoiding of mechanical damage while loading and transportation, plates stacked in the following amounts:
P mark plate, thickness: 10±0,3 mm — 46 PCs
P mark plate, thickness: 12±0.3 mm — 39 PCs
P mark plate, thickness: 16±0,3 mm — 29 PCs
P mark plate, thickness: 18±0.3 mm — 26 PCs
P mark plate, thickness: 22±0,3 mm — 22 PCs
P mark plate, thickness: 24±0.3 mm — 20 PCs
P mark plate, thickness: 26±0.3 mm — 18 PCs
PS mark plate, thickness: 18±0.8 mm — 26 PCs
Packs of plates are lined with packing plates made of chipboard waste and then tightened with a packing tape (2 longitudinal and 4 transverse belts).